96% Alumina Ceramics Filament Assembly for Iron Trap Device (IDT)

• Application: Aerospace, Ceramic Decorations, Electronics, Medical, Brazing, Feedthrough
• Material Composition: Alumina, Al2O3
• Speciality: High Insulation, High Strength, Temperature Resistant
• Type: Ceramic-to-Metal
• Compressive Strength: 2300MPa
• Chemical Resistance: Excellent
• Mechanical Strength: Excellent
• Color: Metal+White
• Thermal Conductivity: 25W/(M.K)
• Processing Service: Moulding
• Max. Use Temperature: 1600ºC
• Density: 3.7g/cm3
• Transport Package: Standard Cartons with Foam
• Specification: Customized
• Trademark: INNOVACERA
• Origin: Fujian, China
• Production Capacity: 200000 Piece/Pieces Per Month

Product Description

Innovacera Advanced Materials is pleased to offer new standard filament assy supports, a critical component in mass spectrometry applications for the analytical and industries. These filament assy supports are manufactured using our 96% alumina ceramics, selected for its good electrical insulation and high temperature stability. Customers can choose between two and four-pin options, with the pins brazed into the alumina insulator ready for filament welding. Innovacera's brazing process makes the filament considerably more resistant to higher temperatures, around 700°C compared with standard adhesives, which can only typically withstand up to 350°C. Many years of manufacturing experience with ceramic-to-metal assemblies means we can work closely with customers to tailor designs to their requirements or produce constant runs of standard designs ensuring quick turnaround and delivery. Ceramic to Metal Brazing (or Soldering) Glass to Metal Sealing Our experienced team of engineers will select the appropriate brazing fixtures, joint design, and process best-suited to your application.
 

 

 

Alumina Ceramic Properties
Properties	Units		Alumina Ceramic
Purity	wt%		95%	99%	99.8%
Volume Density	g/cm3		3.65	3.8	≥3.89
Water Absorption	%		0	0	0
Crystal Size(Grain Size)	μm		4-5	4-5	4-5
Vickers Hardness, HV1.0	Gpa		14	1600	≥15
Flexural Strength	Mpa		300	310	≥300
Coefficient of Linear Expansion	20-500ºC	1x10-6 mm/ºC	6.5-7.5	6.5-7.5	6.5~7.5
	20-800ºC		6.5-8.0	6.5-8.0	6.5~8.0
Thermal Conductivity	W/m·K( 20ºC)		20	25	≥20.9
Specific Heat Capacity	KJ/(kg·K)		≥0.8	≥0.8	≥0.8
Dielectric Strength	KV/mm		≥12	15*106	≥12
Volume Resistivity	Ω·cm 20ºC		≥1014	≥1014	≥1014
	Ω·cm 300ºC		≥1011	≥1011	≥1011
	Ω·cm 500ºC		≥109	≥109	≥109
Dielectric Constant	1MHz		9	9-10	9-10
Tangent of Dielectric Loss	1MHz		≤4x10-4	≤2x10-4	≤3x10-4
Surface Roughness	μm		0.4 After Machine	0.1-0.4 After Machine	0.1-0.4 After Machine
Max Working Temperature	ºC		1600	1600	1650