Application: | High-Pressure Seals, Mechanical Seals, Rotary Seals |
---|---|
Material: | Alumina Ceramic |
Compressive Strength: | 2300MPa |
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Ceramic to metal seals are hermetic joints created by fusing ceramic components to metal substrates using a variety of joining techniques. These seals are renowned for their exceptional heat resistance, chemical stability, and mechanical durability. They're able to withstand extreme temperatures and harsh environments, making them ideal for use in high-performance applications.
Brazing Technology is a crucial aspect of the manufacturing process of ceramic to metal seals. Brazing involves the use of a filler metal, which has a lower melting point than the base materials, to bond the ceramic and metal components together. This process creates a strong, reliable joint that maintains the integrity of both materials.
Material
|
Alumina/BeO/AlN
|
Coating Layer
|
Mo/Mn
Thickness:8-30μm
|
Plated Layer
|
Nickel, Copper, Gold, etc.
Thickness: 2-9μm
|
Treatment
|
Glazed, polishing
|
Dimension
|
Customized
|
Joining types
|
|
Ceramic + Mo/Mn Metallized + plating Ni
|
|
Ceramic + Mo/Mn Metallized + plating Ag
|
|
Ceramic + Mo/Mn Metallized + plating Au
|
|
Ceramic + printing Ag
|
> Feedthrough
> Metal/alloy ceramic metallized
> Screen Printing
> Roll Printing
> Hand Painting
> Air Brush Spraying
> Immersion
> Centrifugal Coating
> Needle Painting
Alumina Ceramic Properties
|
|||||
Properties
|
Units
|
Alumina Ceramic
|
|||
Purity
|
wt%
|
95%
|
99%
|
99.8%
|
|
Volume Density
|
g/cm3
|
3.65
|
3.8
|
≥3.89
|
|
Water Absorption
|
%
|
0
|
0
|
0
|
|
Crystal Size(Grain Size)
|
μm
|
4-5
|
4-5
|
4-5
|
|
Vickers Hardness, HV1.0
|
Gpa
|
14
|
1600
|
≥15
|
|
Flexural Strength
|
Mpa
|
300
|
310
|
≥300
|
|
Coefficient of Linear
Expansion |
20-500ºC
|
1x10-6 mm/ºC
|
6.5-7.5
|
6.5-7.5
|
6.5~7.5
|
20-800ºC
|
6.5-8.0
|
6.5-8.0
|
6.5~8.0
|
||
Thermal Conductivity
|
W/m·K( 20ºC)
|
20
|
25
|
≥20.9
|
|
Specific Heat Capacity
|
KJ/(kg·K)
|
≥0.8
|
≥0.8
|
≥0.8
|
|
Dielectric Strength
|
KV/mm
|
≥12
|
15*106
|
≥12
|
|
Volume Resistivity
|
Ω·cm 20ºC
|
≥1014
|
≥1014
|
≥1014
|
|
Ω·cm 300ºC
|
≥1011
|
≥1011
|
≥1011
|
||
Ω·cm 500ºC
|
≥109
|
≥109
|
≥109
|
||
Dielectric Constant
|
1MHz
|
9
|
9-10
|
9-10
|
|
Tangent of Dielectric Loss
|
1MHz
|
≤4x10-4
|
≤2x10-4
|
≤3x10-4
|
|
Surface Roughness
|
μm
|
0.4 After Machine
|
0.1-0.4 After Machine
|
0.1-0.4 After Machine
|
|
Max Working Temperature
|
ºC
|
1600
|
1600
|
1650
|