Refractory Magnesium Stabilized Zirconia Ceramic Tube Sleeve Bush Pipe

• Application: Aerospace, Electronics, Medical, Industrial Ceramic
• Flexural Strength: >1000 MPa
• Purity: 95%
• Type: Ceramic Parts
• Color: Yellow/White
• Density: 4.6-5.6%
• Porosity: 1-18.5%
• Zro2: 60-95%
• Al2O3: 0.2-20%
• Sio2: 0.2-1%
• MGO: MGO/Y2o3
• Fe2o3: 0.1-0.3%
• TiO2: 0.1-1.0%
• Application Temperature: 0°c-2200ºC
• Applicable Environment: Air, Vacuum, or Atmosphere Protection Environment
• Transport Package: Standard Cartons with Foam
• Specification: Customized
• Trademark: INNOVACERA
• Origin: Fujian, China
• Production Capacity: 20000 Piece/Pieces Per Month

Product Description

Magnesium Stabilized Zirconia Ceramic Tube

Magnesia Stabilized Zirconia (MSZ) is a great refractory and insulating material due to high oxygen ion conductivity, high strength and toughness, and good thermal shock resistance. It has a clean melt at temperatures above 1900°C and above and is specially manufactured for melting superalloys and precious metals. Its superior thermal shock resistance to temperatures reaching up to 2200°C.

Advantages

* High thermal shock resistance
* High wear-resistant and erosion-resistant
* Metal corrosion resistance in high temperature
* Excellent non-wetting characteristics
* High strength
* Long service life
* The stabilizers and grains combination can be designed according to customer's using environment.

Application Temperature
0°C-2200

Applicable Environment
Air, Vacuum, or Atmosphere Protection Environment
 

Application Field

High temperature melt flow control
Sizing nozzle, Ladle skateboard panel, Converter slag blocking slide plate and ring, etc.
Specialty glass manufacturing
Large size high content of zirconia and alumina ceramics, etc.
Metal powder industry
Setter plate, Gas atomizing nozzle, etc.
Precious metal smelting industry
Ceramic Crucibles, etc.
Artificial/Laser Crystal Ceramic Temperature Field
Rare earth composite oxide solid solution ceramic temperature field, etc

 

 

Technical Indicators
Indicators	ltem	Units	MSZ-H	MSZ-L	Custom
Main Composition	ZrO2	%	≥95	≥95	60-95
	AI203	%	≤0.2	≤0.2	0.2-20
	SiO2	%	≤0.4	≤0.4	0.2-1
	MgO	%	≤2.9	≤2.9	MgO/Y203
	Fe203	%	≤0.1	≤0.1	0.1-0.3
	TiO2	%	≤0.1	≤0.1	0.1-1.0
Physical	Color	-	Yellow	Yellow	Yellow/White
	Density	g/cm3	≤5.2	5.4-5.60	4.6-5.6
	Porosity	%	≤18.5	≤8	1-18.5
The stabilizers, grains combination and porosity can be designed according to customer's using environment.