Magnesium Stabilized Zirconia Gas Atomizing Nozzles for Powder Metallurgy

• Application: Aerospace, Electronics, Medical, Industrial Ceramic
• Flexural Strength: >1000 MPa
• Purity: 95%
• Type: Ceramic Parts
• Color: Yellow/White
• Density: 4.6-5.6%
• Porosity: 1-18.5%
• Zro2: 60-95%
• Al2O3: 0.2-20%
• Sio2: 0.2-1%
• MGO: MGO/Y2o3
• Fe2o3: 0.1-0.3%
• TiO2: 0.1-1.0%
• Application Temperature: 0°c-2200ºC
• Applicable Environment: Air, Vacuum, or Atmosphere Protection Environment
• Transport Package: Standard Cartons with Foam
• Specification: Customized
• Trademark: INNOVACERA
• Origin: Fujian, China
• Production Capacity: 20000 Piece/Pieces Per Month

Product Description

MAGNESIUM STABILIZED ZIRCONIA GAS ATOMIZING NOZZLES For Powder Metallurgy

Gas atomization powdering is to smelt the metal alloy and flow it out through a nozzle (leak]. At the nozzle outlet. the liquid metal is atomized by high-speed airflow, and then rapidly condensed to obtain formed powder.

Mainly used in the powder metallurgy industry, ferrous and non-ferrous metal powder smelts, such as copper powders nickebased alloy powders,stainless steel powders, iron powders and other super alloy powders, etc.

Max using temperature: 2200C

Applicable environment: air, vacuum. or atmosphere protection environment.

 

 

Prime Features

> Metal corrosion resistance in high temperature > Wear-resistant and erosion-resistant to metal liquids > High thermal shock resistance > The stabilizers and grains combination can be designed according to customer's using environment.
 

 

Indicators	Item	Units	MSZ-H	MSZ-L	Custom
Main Composition	ZrO2	%	≥95	≥95	60-95
	Al2O3	%	≤0.2	≤0.2	0.2-20
	SiO2	%	≤0.4	≤0.4	0.2-1
	MgO	%	≤2.9	≤2.9	MgO/Y2O3
	Fe2O3	%	≤0.1	≤0.1	0.1-0.3
	TiO2	%	≤0.1	≤0.1	0.1-1.0
Physical	Color	-	Yellow	Yellow	Yellow/White
	Density	g/cm3	≤5.2	5.4-5.60	4.6-5.6
	Porosity	%	≤18.5	≤8	1-18.5
The stabilizers, grains combination and porosity can be designed according to customer's using environment.