Zirconia Ceramic Setting Ring / Ring Gauge Accessories for Inside Micrometers / Holtest and Dial Bore Gages

• Application: Aerospace, Electronics, Medical, Refractory, Industrial Ceramic
• Material: Zirconia
• Processing Service: Moulding
• Surface Roughness: Not More Than Ra0.1um
• Straight Angle: 0.05/φ100
• Parallelism: Not More Than0.015mm
• Hardness: 1200hv
• Inner Diameter Tolerance: ±1um / ±1.5um
• Outer Diameter Tolerance: ±1um / ±1.6um
• Roundness: 0.5um / 0.8um
• Dimensional Interval: 0.5mm
• Type: Ceramic Rings
• Transport Package: Standard Cartons with Foam
• Trademark: INNOVACERA
• Origin: Fujian, China
• Production Capacity: 20000 Piece/Pieces Per Month

Product Description

 

Zirconia Ceramic Plain Ring Gauge

 

Innovacera developed a series of ceramic accessories for Inside Micrometers, Holtest and Dial Bore Gauges. The ceramic material used mostly is zirconia.

 

The zirconia ceramic setting ring advantages: > High wear resistance and long service life > The coefficient of thermal expansion is very small, the effect of temperature is very small > The hardness is very high, there is no need to worry about surface scars > Ring gauge management is simple (regular inspection interval is long, saving cost)

The Zirconia Ceramic Ring Gauges Technology: * Surface Roughness: Not more than Ra0.1um * Straight Angle: 0.05/φ100 * Parallelism: Not more than0.015mm * Each 0.5mm as one size, from 1mm to 50mm.

 

Size	Dimensional interval	Roundness	Outer diameter tolerance:	Inner diameter tolerance	Hardness
1-29mm	0.5mm	0.5um	±1um	±1um	1200HV
30-50mm	0.5mm	0.8um	±1.6um	±1.5um	1200HV

Some Zirconia Ceramic Ring Gauges Innovacera made and size detail: 9mm, 10mm, 18mm, 20mm, 24mm, 25mm, 28mm

D(mm)	d(mm)	T(mm)	outer chamfer(mm)	inner chamfer(mm)
1-2	22	4	0.4	0.3
2.5-4.5	22	5	0.4	0.3
5-9.5	32	8	0.8	0.5
10-14.5	38	10	1.2	0.5
15-19.5	45	12	1.2	1.0
20-24.5	53	14	1.2	1.0
25-31.5	63	16	1.5	1.0
32-39.5	71	18	2.0	1.0
40-50	85	20	2.0	1.0

Zirconium oxide Ceramic Ring Gages Drawing
 

 

 

Zirconia Ceramic Properties:

Item	Value
ZRO2	94.9%
Y2O3	5.4%
HardnessHRA	88-90
Density(g/cm3)	5.5-6.05
Flexural strength (MPA)	1100
Young's Modulus (Gpa)	220
Thermal Expansion Coefficient(20-1000) (×10-6/K)	6.5-11.2
Flexural Toughness(Mpa m1/2)	12