Y-Tzp Zro2 Zirconia Ceramic Rotary Blade

• Application: Aerospace, Electronics, Home Use, Medical, Refractory, Industrial Ceramic
• Flexural Strength: 1000
• Type: Ceramic Parts
• Thermal Shock Resiatance: 350 T(C)
• Color: White
• Compressive Strength: 2000 - 2500 MPa
• Model NO.: Ceramic Snap-off Blade
• Water Absorption: 0
• Thermal Conductivity: 13-27MPa
• Processing Service: Cutting, Moulding
• Volume Resistivity: >10^13
• Maximum Use Temperature: 1000°c
• Vickers Hardness: 12.7gpa
• Transport Package: Standard Cartons with Foam
• Trademark: INNOVACERA
• Origin: Fujian, China
• Production Capacity: 100000 Piece/Pieces Per Month

Product Description

 

Ceramic Rotary Blades are very suitable for fibers, tapes, film, leather, paper cutting machine application. Our material is yttrium stabilizes zirconia ceramic. Unlike other ceramic matetials, Zirconia ceramic is a material with high flexural roughness.Therefore it is not fragile and proper for producing blades. Another advantage is very sharp. Cutting performace is better than Tungsten carbide.

 

Features:
1. Faster cutting rates
2. Consistently good cutting quality, e.g. improved strength of spliced connections
3. No corrosion
4. Smooth running
5. Extended maintenance intervals
6. Universal cleaning possibilities using acids, alkaline solutions and organic solvents

 

Industry:

The range of applications for our ceramic cutters used as shears, blades, knives or circular cutters in Industry as below;
>Textile Industry
>Medical
>Paper
>Semiconductor
>Automotive
>Chemical Fibers
>Film and Foil
>Fiberglass
>Artword and DIY
>Food and beverage production

 

Ceramic material composition:

· 95%--99.99% Alumina (Al2O3)
· Silicon Carbide · Silicon Nitride
· TTZ: Magnesia partially stabilized Zirconia (ZrO2)
· YTZP: Yttria partially stabilized Zirconia (ZrO2)
· ZDY: Yttria fully stabilized Zirconia (ZrO2)

 

Zirconia Ceramic Properties:
 

Item	Value
ZRO2	94.9%
Y2O3	5.4%
HardnessHRA	88-90
Density(g/cm3)	5.5-6.05
Flexural strength (MPA)	1100
Young's Modulus (Gpa)	220
Thermal Expansion Coefficient(20-1000) (×10-6/K)	6.5-11.2
Flexural Toughness(Mpa m1/2)	12